For those who have been searching for an alternative metal wedding ring because you wanted something which is ultimately strong, easy to maintain, fairly inexpensive, and also have been considering one produced from Tungsten Carbide, you have to read this article first! There are a few essential things that you should consider before making your purchase. Like the love and commitment between you and your spouse, the wedding band should last a lifetime. Because of this, Tungsten Carbide may not be the best option for Tungsten Wedding Ring.
The claims that Tungsten Carbide manufacturers make regarding their jewelry are not entirely true and also have been disproven by various strength tests. Once the metal was initially released to the jewelry scene, the dealers claimed that it was indestructible and would maintain a permanent polish. They say that Tungsten Carbide helps make the most wear-resistant wedding band in the world. Sure, Tungsten Carbine rings can remain very shiny throughout their lifetime, but what good is a high polished wedding band which has a large chip or crack?
Not the Most Wear-Resistant on Earth:
Wedding rings are worn on a regular basis and receive plenty of damage. While it is near impossible to scratch a Tungsten Carbide wedding ring, it could actually chip or break fairly easily. In case your Tungsten Carbide wedding ring falls to some hard floor, like one made from stone, it is very prone to shatter into pieces. It is because Tungsten Carbide will not be a metal alloy, however the blend of Tungsten and Carbide powders. This creates microscopic voids in the wedding band and weakens the item.
Impossible to correct:
Another drawback is that Tungsten Carbide rings can not be resized or repaired. You are going to wear your wedding band for a very long time, in fact it is most likely that your finger size may change. Some Tungsten Carbide wedding ring retailers promise to switch your ring if any damage occurs, or maybe your finger shrinks or grows and you need an alternate size, you are going to sometimes be receiving a brand new ring, and not the meaningful piece of jewelry that the spouse placed on your finger the morning of your own wedding.
Here is where softer precious metals would be a better choice. Sure, they are able to scratch or knick easily, but they actually last longer. While wedding rings made from precious metals such as gold, silver, and platinum need regular polishing, they can be repaired and easily resized, and therefore there is no have to completely replace one.
Other Metals to Consider:
Stainless-steel wedding bands are very strong and a lot more resistant against scratching than gold, silver, or platinum. They are some of the least expensive possibilities on the market, and since using the metal for women wedding bands is a contemporary trend, there are lots of fashionable varieties of stainless-steel rings available.
Titanium is probably the strongest metals designed for wedding rings, is 100% hypoallergenic, light in weight, and will be engraved. Titanium wedding bands can also be easily adjusted to suit gfnypb repaired if damaged, and like stainless, they are less expensive and are available in a multitude of design options.
Silversmith Peter Johns created this revolutionary metal in the 1990s. This contemporary silver alloy is a mixture of silver, copper, and germanium; the germanium boosts the metal’s strength and tarnish resistance. Argentium silver is twice as hard as traditional silver, much less labor intensive to produce, and keeps a lasting finish. Argentium silver will be utilized in anything from wedding rings to works of art, as well as musical instruments.
Before considering women tungsten wedding bands, consider one of these other metal types. It will be possible to safely wear your ring made from any one of these alternative metals on a daily basis and not have to worry about the wedding band cracking or chipping.